无银铜基钎料
牌号 Alloy No.
|
国内外 牌号 The national and foreign standards
|
化学成分 % Chemical Composition
|
熔化 温度 ℃ Melting Range
|
Cu |
P |
Sn |
Ni |
HYCuP |
- |
余量 Rem- ainder |
6.8 ~ 7.5 |
- |
- |
710 ~ 800 |
特性/用途: Application: 钎料流动性能好,适用于钎焊不受冲击载荷的铜及铜合金。 Braze filler has good flow properties, which is suitable for brazing copper and copper alloys from impact loads. |
牌号
|
国内外 牌号
|
化学成分
|
熔化 温度
|
Cu |
P |
Sn |
Ni |
HYCu PSn |
- |
余量 Rem- ainder |
5.5 ~ 6.5 |
3.5 ~ 4.5 |
- |
630 ~ 720 |
特性/用途: Application: 钎料流动性能好,可部分代替银钎料和铜磷银钎料钎焊铜及铜合金。 Braze filler has good flow properties, which can partially replace silver brazing filler, copper and phosphor replace silver brazing copper and copper alloys. |
牌号
|
国内外 牌号
|
化学成分
|
熔化 温度
|
Cu |
P |
Sn |
Ni |
HYCuP SnNi-1 |
- |
余量 Rem- ainder |
5.5 ~ 6.5 |
5.0 ~ 6.0 |
0.4 ~ 0.6 |
585 ~ 640 |
特性/用途: Application: 熔点很低,钎焊工艺性能好,适宜于电子器件中银触点和铜合金的钎焊。 Having Low metting point, good brazing it is suitable for electronic devices pieces of silver and copper alloy contacts brazing. |
牌号
|
国内外 牌号
|
化学成分
|
熔化 温度
|
HYCu Sn8P |
- |
余量 Rem- ainder |
0.05 ~ 0.35 |
7.0 ~ 9.0 |
- |
875 ~ 1025 |
特性/用途: Application: 适用于铜与铜锡合金,铜锌合金和铜的焊接,并适合铜与铸件的补焊(适用于炉中钎焊)。 Apply to copper and copper-tin alloy, brazing between copper-zinc alloy and steel and also brazing between copper castings. |
牌号
|
国内外 牌号
|
化学成分
|
熔化 温度
|
Cn |
Zn |
Sn |
Si (Mn) |
HY221 |
BCu60 ZnSn(Si) |
59 ~ 61 |
余量 Rem- ainder |
0.8 ~ 1.2 |
0.15 ~ 0.35 |
890 ~ 905 |
特性/用途: Application: 具有良好的机械性能,用于钎焊铜、钢、铜镍合金、灰口铸铁以及镶嵌硬质合金刀具等。 It has excellent mechanical properties, which is used for brazing copper, steel, copper-nickel alloy, gray cast iron and inlaid carbide cutting tools, etc. |
牌号
|
国内外 牌号
|
化学成分
|
熔化 温度
|
HYCu 58ZnMn |
BCu58 ZnMn |
57 ~ 59 |
余量 Rem- ainder |
- |
3.7 ~ 4.3 (Mn) |
880 ~ 909 |
特性/用途: Application: 接头强度高,适用于500℃以上大负荷工作条件,常用于硬质合金刀具钎焊材料。 Having high strength brazed joints for temperatures above 500 degrees high load operating conditiongs, it often apply to the brazing filer Carbide Tool. |
*本册内容为各类中的部分代表产品
含银铜基钎料
牌号 Alloy No. |
国内外 牌号 The national and foreign standards |
化学成分 Chemical Composition |
熔化 温度 Melting Range |
Cu |
P |
Ag |
HYCuAg2 |
BCu91 PAg |
余量 Rem- ainder |
6.8~ 7.2 |
1.8~ 2.2- |
643~ 788 |
特性/用途: Application: 钎料工艺性能好,适宜于电冰箱、空调器、电机和仪表等行业中的铜和铜合金的钎焊。 Haveing good brazing properties, it is suitable for brazing copper and copper alloy products, such as refrigerators, air conditioning, electrical and instrument manufacturing industry.
|
牌号
|
国内外 牌号
|
化学成分
|
熔化 温度
|
Cu |
P |
Ag |
HYCuAg5 |
BCu89 PAg |
余量 Rem- ainder |
5.8~ 6.2 |
4.8~ 5.2 |
645~ 815 |
特性/用途: Application: 钎焊接头的强度、塑性、导电性及漫流性较好,适用于铜及铜合金的钎焊。 Strength of brazed joins, plastic, electrical conductivity and good flowability for copper and copper alloy brazing. |
牌号
|
国内外 牌号 |
化学成分 |
熔化 温度 |
Cu |
P |
Ag |
HYCuAg15 |
BCu80 AgP |
余量 Rem- ainder |
4.8~ 5.2 |
14.5~ 15.5 |
645~ 800 |
特性/用途: Application: 适宜于钎焊要求比BCu89PAg高的场合。 Applicable to brazing requirements which is higher than BCu89PAg. |
牌号
|
国内外 牌号 |
化学成分 |
熔化 温度 |
Cu |
P |
Ag |
HYCuAg20 |
- |
余量 Rem- ainder |
5.8~ 6.7 |
19~ 21 |
645~ 710 |
特性/用途: Application: 适宜于钎焊要求比BCu89PAg高的场合 Applicable to brazing requirements which is higher than BCu89PAg。
|
牌号
|
国内外 牌号 |
化学成分 |
熔化 温度 |
Cu |
P |
Ag |
HYCuAg25 |
- |
余量 Rem- ainder |
4.5~ 5.5 |
24.5~ 25.5 |
650~ 710 |
特性/用途: Application: 钎焊接头的综合性能是铜磷银钎料中最好的一种,适宜于钎焊要求高的电器接头(银石墨、银钨、银碳化钨等复合材料)。 Overal performance of brazed joints are the best one of silver-copper-phosphorus brazing series. It is appied to high electrcal joints, such as, Silver-Graphte, Silver-lungsten, Silver-lungsten cartride and other composite matenials. |
*本册内容为各类中的部分代表产品
|
|
|