含Ni钎料
牌号 Alloy No.
|
国内外 牌号 The national and foreign standards
|
化学成分% Chemical Composition
|
熔化 温度 ℃ Melting Range
|
Ag |
Cu |
Zn |
In |
HYAg 18In |
- |
17.0 ~ 19.0 |
46.0 ~ 48.0 |
余量 Rem- ainder |
0.8 ~ 1.2 |
792 ~ 810 |
特性/用途: Application: 钎焊工艺性能良好,属推广应用钎料,适宜于机械、制冷等产品的零部件钎焊。 Having good brazing properties, promoting brazing filer for machinery, it is applied to brazing parts products of refrigeration and other industries. |
牌号
|
国内外 牌号
|
化学成分
|
熔化 温度
|
Ag |
Cu |
Zn |
In |
HYAg 30In |
BAg30 CuZnIn |
29.0 ~ 31.0 |
37.0 ~ 39.0 |
25.5 ~ 28.5 |
4.5 ~ 5.5 |
640 ~ 755 |
特性/用途: Application: 适宜于机械、制冷等产品的零部件钎焊。 Applied to brazing parts products of refrigeration and other industries. |
牌号
|
国内外 牌号
|
化学成分
|
熔化 温度
|
Ag |
Cu |
Zn |
In |
HYAg 34In |
BAg34 CuZnIn |
33.0 ~ 35.0 |
34.0 ~ 36.0 |
28.5 ~ 31.5 |
0.8 ~ 1.2 |
660 ~ 740 |
特性/用途: Application: 属推广应用钎料,适宜于机械、制冷等产品的零部件钎焊。 Promoting brazing filler for brazing parts products of machinery, refrigeration and other industries. |
牌号
|
国内外 牌号
|
化学成分
|
熔化 温度
|
Ag |
Cu |
Zn |
In |
HYAg 38In |
- |
37.5 ~ 38.5 |
29.0 ~ 31.0 |
29.0 ~ 31.0 |
1.8 ~ 2.2 |
660 ~ 720 |
特性/用途: Application: 温度低,流动性好,适用于铜合金与钢,黄铜阀体与不锈钢焊接,铜与铁管焊接。 It has low temperature, fiuidity for brazing between copper alloy and steel, brass body and stainless steel, copper and iron pipe. |
牌号
|
国内外 牌号
|
化学成分
|
熔化 温度
|
Ag |
Cu |
Zn |
In |
HYAg 40In |
BAg40 CuZnIn |
39.0 ~ 41.0 |
29.0 ~ 31.0 |
23.5 ~ 26.5 |
4.5 ~ 5.5 |
635 ~ 715 |
特性/用途: Application: 温度低,流动性好,适用于铜合金与钢,黄铜阀体与不锈钢焊接,铜与铁管焊接。 It has low temperature, fiuidity for brazing between copper alloy and steel, brass body and stainless steel, copper and iron pipe. |
*本册内容为各类中的部分代表产品
含Ni/Mn钎料
牌号 Alloy No.
|
国内外 牌号 The national and foreign standards
|
化学成分 % Chemical Composition
|
熔化 温度 ℃ Melting Range
|
Ag |
Cu |
Zn |
Sn |
In |
HYAg 40Ni |
BAg40 CuZnNi |
39.0 ~ 41.0 |
29.0 ~ 31.0 |
26.0 ~ 30.0 |
1.5 ~ 2.5 |
- |
670 ~ 780 |
特性/用途: Application: 具有较好的抗蚀性、适用于不锈钢的焊接和镍基合金及碳化钨的焊接。 Having good corrosion resistance, it is suitable for stainless steel and nickel-based alloys and brazing tungsten carbide. |
牌号
|
国内外 牌号
|
化学成分
|
熔化 温度
|
Ag |
Cu |
Zn |
Sn |
In |
HYAg 50Ni |
- |
49.0 ~ 51.0 |
余量 Rem- ainder |
27.0 ~ 29.0 |
1.5 ~ 2.5 |
- |
660 ~ 750 |
特性/用途: Application: 适用于不锈钢钎焊,提高抗缝隙腐蚀能力。 Applied to stainiess steel brazing and improve resistance to crevice corrosion. |
牌号
|
国内外 牌号
|
化学成分
|
熔化 温度
|
Ag |
Cu |
Zn |
Sn |
In |
HYAg 54Ni |
BAg54 CuZnNi |
53.0 ~ 55.0 |
37.5 ~ 42.5 |
4.0 ~ 6.0 |
0.5 ~ 1.5 |
- |
720 ~ 855 |
特性/用途: Application: 具有较好的抗蚀性、适用于钎焊铜、铜合金、钢及不锈钢 Having good corrosion resistance, it is suitable for brazing copper, copper alloy, steel and stainiess steel |
牌号
|
国内外 牌号
|
化学成分
|
熔化 温度
|
Ag |
Cu |
Zn |
Sn |
In |
HYAg 25NiMn |
BAg25Cu ZnMnNi |
24.0 ~ 26.0 |
37.0 ~ 39.0 |
31.0 ~ 35.0 |
1.5 ~ 2.5 |
1.5 ~ 2.5 |
705 ~ 800 |
特性/用途: Application: 价格便宜,适宜于低端硬质合金工具的钎焊 Having cheap price, it is suitable for general brazing carbide |
牌号
|
国内外 牌号
|
化学成分
|
熔化 温度
|
Ag |
Cu |
Zn |
Sn |
In |
HYAg 49Ni |
BAg49Zn CuMnNi |
48.0 ~ 50.0 |
15.0 ~ 17.0 |
21.0 ~ 25.0 |
4.0 ~ 5.0 |
7.0 ~ 8.0 |
680 ~ 705 |
特性/用途: Application: 对硬质合金的润湿能力强,适宜于硬质合金工具的钎焊。 Having right Carbide wetting ability, it is suitable for brazing carbide tools. |
*本册内容为各类中的部分代表产品
含镉钎料
牌号 Alloy No.
|
国内外 牌号 National Standard
|
化学成分% Chemical Composition
|
熔化 温度 ℃ Melting Range
|
Ag |
Cu |
Zn |
Cd |
Ni |
HYAg 20Cd |
BAg20 CuZnCd |
19.0 ~ 21.0 |
39.0 ~ 41.0 |
23.0 ~ 27.0 |
13.0 ~ 17.0 |
- |
605 ~ 765 |
特性/用途: Application: 熔点较低,漫流性好,适宜于钎焊合金、钢及不锈钢 Having low melting point, good flowability, it is suitable for brazing alloy steel and stainless steel, etc. |
牌号
|
国内外 牌号
|
化学成分
|
熔化 温度
|
Ag |
Cu |
Zn |
Sn |
Ni |
HYAg 30Cd |
BAg30 CuZnCd |
29.0 ~ 31.0 |
26.5 ~ 28.5 |
20.0 ~ 24.0 |
19.0 ~ 21.0 |
- |
607 ~ 710 |
特性/用途: Application: 熔点较低,润湿及填缝性能好,适宜于钎焊铜合金及钢等 Having low melting point, wettabity and good sealing properties, it is suitable for brazing copper alloy and steel, etc. |
牌号
|
国内外 牌号
|
化学成分
|
熔化 温度
|
Ag |
Cu |
Zn |
Sn |
Ni |
HYAg 35Cd |
BAg35 CuZnCd |
34.0 ~ 36.0 |
25.0 ~ 27.0 |
19.0 ~ 23.0 |
17.0 ~ 19.0 |
- |
605 ~ 700 |
特性/用途: Application: 结晶间隔大,适宜于用火焰、高频等钎焊方法进行不均匀间隙的钎焊 It has crystalization interval, which is suitable for brazing method of the uneven gap brazing such 按时 frame, high frequency and so on. |
牌号
|
国内外 牌号
|
化学成分
|
熔化 温度
|
Ag |
Cu |
Zn |
Sn |
Ni |
HYAg 40Cd |
BAg40 CuZnCd |
39.0 ~ 41.0 |
18.0 ~ 20.0 |
19.0 ~ 23.0 |
18.0 ~ 22.0 |
- |
595 ~ 630 |
特性/用途: Application: 熔化温度很低,钎焊性能好,适宜于要求钎焊温度低的材料 Having low melting temperature and good brazing properties, it is applied to low temperature brazing material |
牌号
|
国内外 牌号
|
化学成分
|
熔化 温度
|
Ag |
Cu |
Zn |
Sn |
Ni |
HYAg 40CdNi |
BAg40Cu ZnCdNi |
39.0 ~ 41.0 |
15.5 ~ 16.5 |
14.5 ~ 18.5 |
25.1 ~ 26.5 |
0.1 ~ 0.3 |
595 ~ 605 |
特性/用途: Application: 熔化温度很低,钎焊性能好,适宜于要求钎焊温度低的材料 Having low melting temperature and good brazing properties, it is applied to low temperature brazing material |
牌号
|
国内外 牌号
|
化学成分
|
熔化 温度
|
Ag |
Cu |
Zn |
Sn |
Ni |
HYAg 50Cd |
BAg50 CdZnCu |
49.0 ~ 51.0 |
14.5 ~ 16.5 |
14.5 ~ 18.5 |
17.0 ~ 19.0 |
- |
625 ~ 635 |
特性/用途: Application: 熔化温度很低,钎焊性能好,钎缝表面光洁,接头强度高,适宜于钎焊铜合金、钢等 Having low melting temperature, good brazing properties, brazing seem smooth surface, high joint strength, it is suitable for brazing copper alloy, steel, etc. |
牌号
|
国内外 牌号
|
化学成分
|
熔化 温度
|
Ag |
Cu |
Zn |
Sn |
Ni |
HYAg 50CdNi |
BAg50Cu ZnCdNi |
49.0 ~ 51.0 |
14.5 ~ 16.5 |
13.5 ~ 17.5 |
15.0 ~ 17.0 |
2.5 ~ 3.5 |
635 ~ 690 |
特性/用途: Application: 有良好的抗腐蚀性及对硬质合金的湿润能力,适宜于硬质合金的钎焊 Having good corrosion resistance, and carbide wetting ability, it is suitable for brazing carbide |
*本册内容为各类中的部分代表产品
含锡钎料
牌号 Alloy No. |
国内外 牌号 The national and foreign standards |
化学成分 % Chemical Composition
|
融化 温度 ℃ Melting Range |
Ag |
Cu |
Zn |
Sn |
Ni |
HYAg 18Sn |
- |
17.5 ~ 18.5 |
余量 Rem- ainder |
32.0 ~ 36.0 |
1.5 ~ 2.5 |
- |
780 ~ 810 |
特性/用途: Application: 价格便宜,熔点较高,但是钎焊工艺性能好,适宜于机械、制冷等产品的零部件钎焊 Having cheap price, high melting point. but good brazing properties. it is suitable for parts products of machinery and refrigeration
|
牌号
|
国内外 牌号
|
化学成分
|
融化 温度
|
Ag |
Cu |
Zn |
Sn |
Ni |
HYAg 25Sn |
BAg25 CuZnSn |
24.0 ~ 26.0 |
39.0 ~ 41.0 |
31.0 ~ 35.0 |
1.5 ~ 2.5 |
- |
680 ~ 760 |
特性/用途: Application: 钎焊工艺性能好,适宜于机械、制冷等产品的零部件钎焊 Having good manufacture brazing process performance, it is suitable for parts products of machinery and refrigeration |
牌号
|
国内外 牌号
|
化学成分
|
融化 温度
|
Ag |
Cu |
Zn |
Sn |
Ni |
HYAg 30Sn |
BAg30 CuZnSn |
29.0 ~ 31.0 |
35.0 ~ 37.0 |
30.0 ~ 34.0 |
1.5 ~ 2.5 |
- |
665 ~ 755 |
特性/用途: Application: 钎焊温度低,漫流工艺性能好,适宜于铜、钢及邦迪管的钎焊。 Having low brazing temperature, good overflow process performance, it is suitable for copper, steel and Bundy tubes brazed. |
牌号
|
国内外 牌号
|
化学成分
|
融化 温度
|
Ag |
Cu |
Zn |
Sn |
Ni |
HYAg 34Sn |
BAg34 CuZnSn |
33.0 ~ 35.0 |
35.0 ~ 37.0 |
25.5 ~ 29.5 |
2.0 ~ 3.0 |
- |
630 ~ 730 |
特性/用途: Application: 钎焊工艺性能好,适宜于铜、钢及邦迪管等的钎焊。 Having good brazing properties, it is suitable for copper, steel and Bundy tubes brazed.
|
牌号
|
国内外 牌号
|
化学成分
|
融化 温度
|
Ag |
Cu |
Zn |
Sn |
Ni |
HYAg 40Sn-2 |
BAg40 CuZnSn |
39.0 ~ 41.0 |
29.0 ~ 31.0 |
26.0 ~ 30.0 |
1.5 ~ 2.5 |
- |
650 ~ 710 |
特性/用途: Application: 熔点低,具有良好的漫流性和填充接头间隙能力,钎缝表面光洁,接头强度高,可替代含镉钎料。 It has low melting point, good flowability and the ability to fill the gap joints, brazing seam smooth surface, high joint strength, which can replace cadmium-containing brazing. |
牌号
|
国内外 牌号
|
化学成分
|
融化 温度
|
Ag |
Cu |
Zn |
Sn |
Ni |
HYAg 45Sn |
BAg45 CuZnSn |
44.0 ~ 46.0 |
26.0 ~ 28.0 |
23.5 ~ 27.5 |
2.0 ~ 3.0 |
- |
640 ~ 680 |
特性/用途: Application: 熔点较低,润湿性及漫流性良好,可替代含镉钎料(312)。 It has low melting point, good wettability and flowability, which can be taken the place of brazing material containing elements of cadmium (312). |
牌号
|
国内外 牌号
|
化学成分
|
融化 温度
|
Ag |
Cu |
Zn |
Sn |
Ni |
HYAg 50Sn |
- |
49.0 ~ 51.0 |
20.5 ~ 22.5 |
余量 Rem- ainder |
0.7 ~ 1.3 |
0.30 ~ 0.65 |
650 ~ 670 |
特性/用途: Application: 钎料熔点低,钎焊工艺性能好,适宜于钎焊铜、钢等要求钎焊温度较低的材料 Havin low melting point, good brazing properties, it is suitable for low temperature brazing meterial requirements, such as brazing copper, steel. |
牌号
|
国内外 牌号
|
化学成分
|
融化 温度
|
Ag |
Cu |
Zn |
Sn |
Ni |
HYAg 56Sn |
BAg56 CuZnSn |
55.0 ~ 57.0 |
21.0 ~ 23.0 |
15.0 ~ 19.0 |
4.5 ~ 5.5 |
- |
620 ~ 655 |
特性/用途: Application: 钎料熔点低,润湿性及漫流性良好,适宜于钎焊铜合金、钢等,特别适于食品工业设备的钎焊 Having low meting point, good wetting and flowability, it is suitable for brazing copper alloys, steel, etc. especially used in the brazing equipment of food industry. |
牌号
|
国内外 牌号
|
化学成分
|
融化 温度
|
Ag |
Cu |
Zn |
Sn |
Ni |
HYAg 60Sn |
BAg60 CuSn |
59.0 ~ 61.0 |
29.0 ~ 31.0 |
- |
9.5 ~ 10.5 |
- |
600 ~ 730 |
特性/用途: Application: 不含易挥发元素,适用于电子器件的保护气氛和真空钎焊 It does not contain volatile elements, which is suitable for electronic devices protective atmosphere brazing and vacuum brazing. |
牌号
|
国内外 牌号
|
化学成分
|
融化 温度
|
Ag |
Cu |
Zn |
Sn |
Ni |
HYAg 63Sn |
- |
62.0 ~ 64.0 |
余量 Rem- ainder |
- |
5.0 ~ 7.0 |
2.0 ~ 3.0 |
691 ~ 802 |
特性/用途: Application: 适用于不锈钢、碳化钨等真空钎焊。 Applied to stainless steel, tungsten carbide vacuum brazingl. |
*本册内容为各类中的部分代表产品
三元系
牌号 Alloy No. |
国内外 牌号 The national and foreign standards |
化学成分 % Chemical Composition |
融化温度 ℃ Melting Range |
Ag |
Cu |
Zn |
HYAg10 |
- |
9.0~ 11.0 |
52.0~ 54.0 |
余量 Rem- ainder |
815~ 850 |
特性/用途: Application: 价格便宜,但钎焊温度较高,接头塑性较差,适用于钎焊要求较低的铜合金、钢等。 It has cheap price requiring a high temperature brazing. The joint is poor ductility, which is suitable for brazing requiring a lower Cooper alloy brazing of steel.
|
牌号
|
国内外 牌号
|
化学成分
|
融化温度
|
Ag |
Cu |
Zn |
HYAg25 |
BAg25 CuZn |
24.0~ 26.0 |
39.0~ 41.0 |
33.0~ 37.0 |
700~ 790 |
特性/用途: Application: 钎焊温度高,润湿性及填缝能力好,适宜钎焊铜合金、钢等。 Having the brazing temperature is slightly higher, good wetting and sealing ability, it is suitable for brazing copper alloy, steel and so on. |
牌号
|
国内外 牌号
|
化学成分
|
融化温度
|
Ag |
Cu |
Zn |
HYAg30 |
BAg30 CuZn |
29.0~ 31.0 |
37.0~ 39.0 |
30.0~ 34.0 |
680~ 765 |
特性/用途: Application: 融化温度低,接头有较好的韧性,适用于铜,铜合金、钢焊接。 Having low melting temperature, brazed joints having good toughness, it is suitable for copper, copper alloy and steel brazing. |
牌号
|
国内外 牌号
|
化学成分
|
融化温度
|
Ag |
Cu |
Zn |
HYAg35 |
BAg35 ZnCu |
34.0~ 36.0 |
31.0~ 33.0 |
31.0~ 35.0 |
685~ 775 |
特性/用途: Application: 中等融化温度低,接头有较好的韧性,适用于铜,铜合金、钢焊接。 Moderate melting temperature, the brazed joint having good toughness, for copper, copper alloy and steel brazing.
|
牌号
|
国内外 牌号
|
化学成分
|
融化温度
|
Ag |
Cu |
Zn |
HYAg45 |
BAg45 CuZn |
44.0~ 46.0 |
29.0~ 31.0 |
23.0~ 27.0 |
665~ 745 |
特性/用途: Application: 熔点较低,润湿性及填缝能力好,接头强度高且能承受振动载荷,适用范围广。 Having low melting point, good wetting and sealing ability, high strength brazed joints under vibration load it is widely applied. |
牌号
|
国内外 牌号
|
化学成分
|
融化温度
|
Ag |
Cu |
Zn |
HYAg50 |
BAg50 CuZn |
49.0~ 51.0 |
33.0~ 35.0 |
14.0~ 18.0 |
690~ 775 |
特性/用途: Application: 具有良好的漫流性和填满间隔能力,钎焊接头强度高,塑性高,适用于钎焊铜及铜合金、钢及不锈钢。 Having good flowability and fill the gap, high strength brazed joints, plastic, it is suitable for brazing copper, copper alloy and stainless steel. |
牌号
|
国内外 牌号
|
化学成分
|
融化温度
|
Ag |
Cu |
Zn |
HYAg60 |
BAg60 CuZn |
59.0~ 61.0 |
25.0~ 27.0 |
12.0~ 16.0 |
695~ 730 |
特性/用途: Application: 铺展性、填缝性好,用于铜及铜合金、钢及不锈钢,镀Sn、Zn钢件等。 It has spreadability, good sealing performance, which can be used for copper and copper alloys, steel and stainless steel, plated Sn, Zn steel pieces and so on. |
牌号
|
国内外 牌号
|
化学成分
|
融化温度
|
Ag |
Cu |
Zn |
HYAg65 |
BAg65 CuZn |
64.0~ 66.0 |
19.0~ 21.0 |
13.0~ 17.0 |
670~ 720 |
特性/用途: Application: 熔点低,漫流性零号,钎缝表面光洁,钎焊接头有良好的强度和塑性,适用于钎焊性能要求较高的铜及铜合金、钢及不锈钢 It has low meting point, good flowability, brazing seam surface brightness, brazed joints with good strength and applied to higher requirements, such as brazing copper and copper alloys, steel and stainless steel. |
*本册内容为各类中的部分代表产品
二元系真空钎料
牌号 Alloy No.
|
国内外 牌号 The national and foreign standards
|
化学成分 % Chemical Composition
|
融化温度 ℃ Melting Range
|
Ag |
Cu |
Li |
HYAg 50Cu |
- |
49.5 ~ 50.5 |
余量 Rem- ainder |
- |
779 ~ 850 |
特性/用途: Application: 不含易挥发元素,适用于电子器件的保护气氛和真空钎焊,分步钎焊中的前步钎焊。 Having Brazing alloy composition does not contain volatie elements, it is suitable for electronic devices to protect the atmosphere and vacuum txazing, brazing stages in the first step brazing. |
牌号
|
国内外 牌号
|
化学成分
|
融化温度
|
Ag |
Cu |
Li |
HYAg 72Cu |
BAg 72Cu |
71.0 ~ 73.0 |
27.0 ~ 29.0 |
- |
779 ~ 779 |
特性/用途: Application: 银铜共晶体钎料,不含易挥发元素,钎焊性好,导电性高,适用于电真空器件中的铜、镍、钛等合金的真空及还原气氛钎焊。 Silver-copper eutectic melting point of the brazing material does not contain volatile elements. It has good brazing performance, high conductivity which for electric vacuum device and vacuum brazing copper, nickel, titanium alloy brazing |
牌号
|
国内外 牌号
|
化学成分
|
融化温度
|
Ag |
Cu |
Li |
HYAg 72CuLi |
BAg 72CuLi |
71.0 ~ 73.0 |
余量 Rem- ainder |
0.25 ~ 0.50 |
766 ~ 766 |
特性/用途: Application: 钎料导电性好,不容易挥发,适用于电子管及真空器件的钎焊,还可钎焊钼,镍及铜等可阀元件。 It has Conductive properties, not easy to be volatile, suitable for brazing of tubes and vacuum device. It can also brazing nickel, molybdenum, and copper and other elements Kovar. |
牌号
|
国内外 牌号
|
化学成分
|
融化温度
|
Ag |
Cu |
Li |
HYAg 92.5CuLi |
BAg-19 |
92.0 ~ 93.0 |
余量 Rem- ainder |
0.15 ~ 0.30 |
760 ~ 891 |
特性/用途: Application: 钎料导电性好,不容易挥发,适用于电子管及真空器件的钎焊,还可钎焊钼,镍及铜等可阀元件。 Having Conductive properties and not easy to be volatile, it id suitable for brazing of tubes and vacuum device. It can also brazing nickel, molybdenum, and copper and other elements Kovar. |
*本册内容为各类中的部分代表产品
|
|
|